The photochemical conversion of methane into methanol from H2O2 aqueous solution as well as the effect of the addition mode were studied. Direct addition of different amounts H2O2 leads to increasing methanol production at the first stage of the reaction. The excess of H2O2 would lead to the reactive oxygen species scavenging and the subsequent O2 production. It was…
Mixed oxides, alpha-Fe2O3/Bi2WO6, were prepared using a mechanical mixing procedure by adding to the Bi2WO6 previously obtained by hydrothermal method the corresponding amount of a prepared alpha-Fe2O3, the latter obtained by thermal decomposition of Fe(NO3)center dot 9H(2)O. The physicochemical surface, structural, morphological characteristics and optical properties of the samples, single and mixed, were determined by…
g-C3N4 and TiO2 hybrid structures are synthesized by means of a simple impregnation method having good photoactivities for the degradation of phenol under UV irradiation. From the wide structural and surface characterization we have stated that the presence of g-C3N4 notably affect the surface feature of TiO2 (surface area and pore size distribution). Enhanced photoactivities…
Dye solar cells consisting of mesoporous TiO 2 nanocolumnar films sensitized with a highly absorptive indoline dye were studied to estimate the charge collection efficiency provided by porous 1-dimensional (1-D) nanostructures in combination with viscous, fast-recombining electrolytes. The TiO 2 mesoporous nanostructured films were prepared by physical vapor deposition at glancing incidence (GLAD-PVD). Electrochemical Impedance…
Silver-TiO2 nanocomposite was prepared by photodeposition of silver nanoparticles on the surface of titanium dioxide. The sonochemical method was used for the deposition of silver-TiO2 powder on commercial foamed waste-glass strips (FWGS). The silver-TiO2 and the coated FWGS was characterized by XRD, DRS, SEM, TEM and nitrogen adsorption. In order to enhance silver-TiO2 deposition, different…
A comparative study of the photodeposition of Pt, Au and Pd under the same experimental conditions onto pre-sulphated and non-sulphated TiO2 was performed. Morphological and surface characterisation of the samples as well as photocatalytic activity for phenol photooxidation was studied. The influence of sulphate pre-treatment on the deposits size and dispersion onto the TiO2 surface,…