This work aims at presenting an innovative method for tailoring the morphology of functionalized plasma polymer films (PPF). The approach is based on the formation of a plasma polymer bilayer system in which the two layers differ by their chemical composition and cross-linking degree. As a case study, propanethiol-based plasma polymer films have been investigated.…
Eu:GdVO4 nanophosphors with an average size of 60 nm, synthesized by a facile solvothermal method, were deposited on monocrystalline silicon wafers by a spray-coating technique with artworks anti-counterfeiting applications in mind. Atmospheric pressure plasma jet (APPJ) was used to deposit a silica-based layer on top of the nanometric luminescent layer, in order to improve its adhesion to…
This work is focused on the transformation of the disordered fluorite cubic-F phase to the ordered cubic-C bixbyite phase, induced by isothermal annealing as a function of the residual stresses resulting from different concentrations of microstructural defects in the yttrium oxide, Y2O3. This transformation was studied using in-situ X-ray diffraction and was modelled using Kolmogorov-Johnson-Mehl-Avrami…
Several mixed oxide thin film series of samples (Si–Co–O, Si–Ni–O, Si–W–O) have been prepared by reactive magnetron sputtering at oblique angle geometries. The paper focuses on the description of microstructure of the films as a function of their stoichiometry. It is found that for identical process parameters (gas mixture, pressure, magnetron-substrate distance, incidence angle of…
The tribological properties of CrAlN, CrAlYN and CrAlZrN coatings deposited by direct current reactive magnetron sputtering are studied by means of pin-on-disc experiments at room temperature, 300, 500 and 650 °C using alumina balls as counterparts. The influence of the metallic composition (Al, Y and Zr) on the friction, wear properties and oxidation resistance is…
This paper reports a systematic analysis of the mechanical properties of nanocolumnar TiO2 thin films prepared by evaporation at a glancing geometry. A systematic study of the mechanical properties is carried out by comparing the hardness and the Young’s modulus determined by nanoindentation for thin films prepared at different deposition angles and characterized by a…
We have studied low refractive index fluorine doped silica thin films prepared by reactive magnetron sputtering. Two experimental parameters were varied to increase the porosity of the films, the geometry of the deposition process (i.e., the use of glancing angle deposition) and the presence of chemical etching agents (fluorine species) at the plasma discharge during…
Previous studies have indicated that long-chain linear carboxylic acids form commensurate packed crystalline monolayers on graphite even at temperatures above their melting point. This study examines the effect on the monolayer formation and structure of adding one or more secondary hydroxyl, functional groups to the stearic acid skeleton (namely, 12-hydroxystearic and 9,10-dihydroxystearic acid). Moreover, a…
Highly oriented CrO2 thin films have been heteroepitaxially grown on TiO2 rutile (110), (100) and (001) single crystalline substrates, by Low Pressure Chemical Vapor Deposition from CrO3 as precursor and flowing oxygen as carrier gas, under a pressure of 67 Pa. The experimental conditions were fine tuned by depositing on polycrystalline Ti foils, to improve the…
Thin (40 nm and 160 nm) CrN coatings were deposited on steel by reactive magnetron sputtering deposition, varying the N2 flow. The coatings were characterized in the as-deposited condition and after annealing in air at 500 °C for 1 h, by X-Ray Diffraction, Transmission Electron Microscopy, Raman and Fourier Transform Infrared spectroscopies. Hardness was measured…