The thermal memory effect, TME, has been studied in Ni55Fe19Ga26 shape memory alloys, fabricated as ribbons via melt-spinning and as pellets via arc-melting, to evaluate its dependence on the martensitic structure and the macrostructure of the samples. When the reverse martensitic transformation is interrupted, a kinetic delay in the subsequent complete transformation is only evident in…
The complete range of Ti5Si3–Ti5Ge3 solid solutions was synthesised from elemental mixtures of Ti, Si, and Ge under an inert atmosphere via mechanically induced self-sustaining reactions (MSR). The stoichiometry of Ti5Si3−xGex solid solutions was controlled by adjusting the Si/Ge ratio of the initial mixture. The chemical composition and lattice parameters of the materials confirmed that…
Titanium and silicon powder blends were ball-milled under an inert atmosphere and subsequently annealed in a nitrogen atmosphere. Ti62.5Si37.5, Ti55.6Si44.4, and Ti50Si50 mixtures suffered a mechanically induced self-propagating reaction during milling. The products of the combustion were Ti5Si3 for the Ti62.5Si37.5 mixture and a combination of intermetallic phases for the Ti55.6Si44.4 and Ti50Si50 mixtures. The Ti33.3Si66.7 blend did not show an MSR process,…