Self-standing films of poly(-hydroxyl hexadecanoic acid) [poly(-OHC16)] have been prepared by noncatalyzed melt-polycondensation in air at 150, 175, and 200 degrees C. Poly(-OHC16)s obtained are characterized as polyesters by infrared spectroscopy (FT-IR) and solid state magic angle spinning C-13 nuclear magnetic resonance (C-13 MAS-NMR). Structurally, poly(-OHC16)s are quite crystalline as revealed by wide angle X-ray diffraction (WAXD). The presence of oxygen in the reaction atmosphere causes a mild oxidation in the form of peroxyester species, tentatively at the interphase between poly(-OHC16) crystallites, and the structure amorphization. The interfacial peroxyester phase ends up in the encapsulation of the polyester grains and provides a barrier towards the action of solvents. Thermal stabilization and insolubility resulting from the synthesis conditions used are interesting features to prepare solvent and heat resistant poly(-OHC16) coatings. Thus, a few microns thick poly(-OHC16) layer has been fabricated on aluminum foil and its resistivity towards a chloroform:methanol (1:1, v:v) mixture has been confirmed.